What are the main components of TTO high-speed coding ribbon?

The main components of TTO high-speed coding ribbon usually include the following parts:

1、Base material

The base layer of TTO high-speed coding carbon tape is generally made of materials such as polyester film (PET). This material has good mechanical properties and chemical stability, capable of withstanding the heat and pressure during the printing process, while ensuring the clarity and durability of printed information.

2、 Ink layer

The ink layer is a key part of TTO high-speed coding ribbon, which determines the quality and adhesion of printed information. The ink layer is usually composed of resin based, mixed based, or wax based inks, which soften and transfer to the surface to be printed when heated. Different types of inks have different characteristics and applicable ranges, such as:

Resin based inks typically have good adhesion and wear resistance, making them suitable for printing tasks that require long-term storage and exposure to harsh environments.

Hybrid ink combines the advantages of resin based and wax based inks, with moderate adhesion and wear resistance, as well as good printing effects and cost-effectiveness.

Wax based inks usually have better printing effects and lower costs, but may be slightly inferior to resin based and mixed based inks in terms of adhesion and wear resistance.

3、 Release agent layer

The release agent layer is usually coated on the back of the ink layer to prevent ink from sticking to the print head during the printing process. The selection and coating quality of the release agent layer are crucial for the protection of the print head and the stability of print quality.

4、 Back coating

The back coating is another important component of TTO high-speed coding ribbon, which mainly serves to lubricate the print head, protect the print head, and prevent static electricity accumulation. The back coating is usually composed of special lubricants, anti-static agents, and other materials, which can ensure the smoothness of the printing process and the long-term service life of the print head.

In summary, the main components of TTO high-speed coding ribbon include base material, ink layer, release agent layer, and back coating. The selection and combination of these components determine the printing effect, adhesion, and wear resistance of the carbon ribbon. When selecting TTO high-speed coding ribbon, it is necessary to choose according to specific printing requirements and material characteristics to ensure the best printing effect and compatibility.